MECHANICALLY-INDUCED HYDROGEN ABSORPTION IN Zr-BASED QUASICRYSTALS / Mulas, G.R.C.E., Pistidda, C., Cocco, G., Scudino, S., Eckert, J.. - In: REVIEWS ON ADVANCED MATERIALS SCIENCE. - ISSN 1606-5131. - 18:7(2008), pp. 645-649.
abstract:
We report on hydrogen sorptive properties of Zr-Ti-Nb-Cu-Al-Ni icosahedral alloys under
different mechanical activation conditions. Two compositions were investigated,
Zr67Ti6.14Nb1.92Cu10.67Ni8.52Al5.75 and Zr57Ti8Nb2.5Cu13.9Ni11.1Al7.5 prepared respectively by partial crystallization
from mechanically alloyed amorphous powders, and by copper mold casting. In the
former, independently by the milling conditions, the gaseous absorption took place with loss of the
icosahedral symmetry and precipitation of a δ-ZrH1.66-type nanocrystalline hydride which accompanied
the formation of an amorphous hydride. Annealing treatments did not permit to restore
initial structural conditions, so hindering the process reversibility. In the latter system, conversely,
hydrogen absorption, activated by mechanical agitation in absence of milling ball, occurred by
retaining the quasiperiodic features, just swelling the icosahedral structure. Thermally activated
desorption preserved the QC symmetry and further successful hydrogenation indicated cycling
possibility, at least partial, of the process. Hydriding kinetics, studied under isobaric conditions,
followed sigmoidal trends, with specific characteristics depending on the alloy stoichiometry and
the activation conditions.
different mechanical activation conditions. Two compositions were investigated,
Zr67Ti6.14Nb1.92Cu10.67Ni8.52Al5.75 and Zr57Ti8Nb2.5Cu13.9Ni11.1Al7.5 prepared respectively by partial crystallization
from mechanically alloyed amorphous powders, and by copper mold casting. In the
former, independently by the milling conditions, the gaseous absorption took place with loss of the
icosahedral symmetry and precipitation of a δ-ZrH1.66-type nanocrystalline hydride which accompanied
the formation of an amorphous hydride. Annealing treatments did not permit to restore
initial structural conditions, so hindering the process reversibility. In the latter system, conversely,
hydrogen absorption, activated by mechanical agitation in absence of milling ball, occurred by
retaining the quasiperiodic features, just swelling the icosahedral structure. Thermally activated
desorption preserved the QC symmetry and further successful hydrogenation indicated cycling
possibility, at least partial, of the process. Hydriding kinetics, studied under isobaric conditions,
followed sigmoidal trends, with specific characteristics depending on the alloy stoichiometry and
the activation conditions.